IFUCAI CELL系列是通用型PVC泡沫产品，可选择密度范围60-300KG/m³，采用了水悬浮发泡工艺，使泡沫交联结构完整化。
■产品特性
- 100%闭孔结构，优越的力学性能
- 良好的耐化学性，可与多种树脂体系兼容
- 良好的介电性能，隔音，隔热
■ 应用领域
- 风电叶片
- 轨道交通
- 游轮船舶
- 汽车制造
- 运动器材
► 产品性能：
-properties of products-
| 测试项目 | 标准 | 单位 | 结果 | D60 | D80 | D100 |
| 密度 | ISO 845 | Kg/ m³ | 平均值 | 62.07 | 80.8 | 101.2 |
| 范围 | 54-69 | 72-92 | 92-108 | |||
| 压缩强度 | ISO 844:2006 | MPa | 平均值 | 0.996 | 1.72 | 2.08 |
| 最小值 | 0.7 | 1.3 | 1.9 | |||
| 压缩模量 | ISO 844:2006 | MPa | 平均值 | 87.4 | 122 | 151 |
| 最小值 | 55 | 75 | 134 | |||
| 剪切强度 | ISO 1922:2012 | MPa | 平均值 | 0.914 | 1.15 | 1.66 |
| 最小值 | 0.7 | 1.0 | 1.4 | |||
| 剪切模量 | SO 1922:2012 | MPa | 平均值 | 26.7 | 33.9 | 42 |
| 最小值 | 22 | 25 | 35 | |||
| 拉伸强度 | ASTM C297 | MPa | 平均值 | 1.81 | 2.66 | 2.96 |
| 最小值 | 1.0 | 2.2 | 2.4 | |||
| 拉伸模量 | ASTM C297 | MPa | 平均值 | 96.1 | 130 | 152 |
| 最小值 | 45 | 85 | 124 |
无论您的选择标准是密度、耐温性、泡孔大小或特定的力学性能，提供的一系列IFUCAICELL产品及IFUCAI-BALSA都能满足您的应用要求。
所有的
IFUCAICELL泡沫，包括密度非常低的产品，都具有优异的力学性能。此外，相比其他硬质泡沫，IFUCAICELL泡沫具有更高的热变形温度和压缩蠕变强度。
IFUCAI cell PVC foam board
1、Type designation: D60, D80
2、Technical Data Sheet
|
Test Item |
Standard |
Unit |
Results |
D60 |
D80 |
|
Density |
ISO 845 |
Kg/ m³ |
Mean |
62.07 |
80.8 |
|
Range |
54-69 |
72-92 |
|||
|
Compressive strength |
ISO 844:2006 |
MPa |
Mean |
0.996 |
1.72 |
|
Msmv |
0.7 |
1.3 |
|||
|
Compressive modulus |
ISO 844:2006 |
MPa |
Mean |
87.4 |
135 |
|
Msmv |
55 |
75 |
|||
|
Shear strength |
ISO 1922:2012 |
MPa |
Mean |
0.914 |
1.15 |
|
Msmv |
0.7 |
1.0 |
|||
|
Shear modulus |
SO 1922:2012 |
MPa |
Mean |
26.7 |
33.9 |
|
Msmv |
22 |
25 |
|||
|
Tensile strength |
ASTMC297 |
MPa |
Mean |
1.81 |
2.66 |
|
Msmv |
1.0 |
2.2 |
|||
|
Tensile modulus |
ASTMC297 |
MPa |
Mean |
96.1 |
130 |
|
Msmv |
45 |
85 |
Definitions
mean = arithmetic mean of type test results
msmv = manufacturer’s specified minimum value
3、Product description
The D60and D80 PVC foam as new high-strength material,with lightweight, high strength, fatigue resistance.
4、Field of application and special limitations of the product
ThePVC foam is compatible with almost all resin systems,whichcan be expanded the application in many filed, not only widely used in wind turbine, high-speed train, the luxurious yacht, aerospace and other cutting-edgefiled,but also many undevelopedfiled of high-end include building fire prevention, heat preservation, sound insulation, etc.
Thefinish productsurface preparationno needs forcoating or seal.
5、The storage condition
1）PVC rigid structure foam should be stored in the ambient temperature is not higher than 40℃, therange of humidity is 5%-75%.
2）In order to avoid the irregular shrinkage of theproduct, theproduct cannot be exposed to direct sunlight, and the ambient temperature and humidity around the foam are kept uniform.
3）When the storage environment is quite different from the workshop , thePVC should bestored in the workshopmore than 24 hours before used.